Field effect transistor assemblies, integrated circuitry, and methods of forming field effect transistors and integrated circuitry

ABSTRACT

The invention encompasses integrated circuitry which includes a semiconductive material substrate and a first field effect transistor supported by the substrate. The first field effect transistor comprises a first transistor gate assembly which includes a first layer of conductively doped semiconductive material and only one layer of conductive nitride. The integrated circuitry further comprises a second field effect transistor supported by the substrate. The second field effect transistor comprises a second transistor gate assembly which includes a second layer of conductively doped semiconductor material and at least two layers of conductive nitride. The invention also encompasses a field effect transistor assembly which includes a channel region and an insulative material along the channel region. The transistor assembly further includes a gate stack proximate the channel region. The gate stack includes a first conductive nitride layer separated from the channel region by the insulative material. The stack further includes a conductively doped semiconductive material proximate the first conductive nitride layer, and a second conductive nitride layer separated from the first conductive nitride layer by the conductively doped semiconductive material. Additionally, the invention encompasses methods of forming field effect transistors, and methods of forming integrated circuitry.

TECHNICAL FIELD

The invention pertains to integrated circuitry, field effect transistor assemblies, methods of forming field effect transistors, and methods of forming integrated circuitry.

BACKGROUND OF THE INVENTION

A prior art semiconductive wafer fragment 10 is shown in FIG. 1. Wafer fragment 10 comprises a memory array region 12 and a region 14 peripheral to memory array region 12. Wafer fragment 10 further comprises a semiconductive material substrate 16. Substrate 16 can comprise, for example, a monocrystalline silicon wafer lightly background doped with a p-type dopant. To aid in interpretation of the claims that follow, the terms “semiconductive substrate” and “semiconductor substrate” are defined to mean any construction comprising semiconductive material, including, but not limited to, bulk semiconductive materials such as a semiconductive wafer (either alone or in assemblies comprising other materials thereon), and semiconductive material layers (either alone or in assemblies comprising other materials). The term “substrate” refers to any supporting structure, including, but not limited to, the semiconductive substrates described above.

A memory array transistor gate 18 is formed over memory array region 12. Transistor gate 18 comprises a stack of materials including a gate dielectric 22, a conductively doped polysilicon 24, a metal silicide 26, and an insulative cap 28. Gate dielectric 22 can comprise, for example, silicon dioxide or tantalum pentoxide. Conductively doped polysilicon 24 can be doped to a concentration of, for example, greater than 10¹⁹ atoms/cm³ with either n-type or p-type conductivity enhancing dopant. Metal silicide 26 can comprise, for example, titanium silicide. Finally, insulative cap 28 can comprise, for example, silicon dioxide or silicon nitride. Alternatively, cap 28 can comprise a stack of materials including an antireflective coating and other insulative materials such as, for example, silicon nitride. The antireflective coating can comprise, for example, a deposited antireflective coating (DARC).

Sidewalls 30 are provided adjacent the transistor gate, and can comprise, for example, silicon dioxide or silicon nitride.

Source/drain regions 32 are provided within substrate 12 proximate gate 18, and together with gate 18 form an operative field effect transistor device 33. Source/drain regions 32 are typically doped with n-type conductivity-enhancing dopant.

A peripheral transistor gate 20 is formed over peripheral region 14. Transistor gate 20 comprises a stack of gate dielectric 40, conductively doped polysilicon 42, metal silicide 44, and an insulative cap 46. Gate dielectric 40, conductively doped polysilicon 42, silicide 44 and insulative cap 46 can comprise materials such as those discussed above pertaining to gate dielectric 22, conductively doped polysilicon 24, silicide 26 and cap 28, respectively.

Sidewalls 48 are provided adjacent gate stack 20, and source/drain regions 50 are provided within substrate 16 proximate to gate stack 20. Source/drain regions 50 and gate stack 20 together form a functional field effect transistor 53. Source/drain regions 50 can be doped with p-type conductivity enhancing dopant or n-type conductivity enhancing dopant to form either a p-type metal-oxide semiconductor (PMOS) or n-type metal-oxide semiconductor (NMOS) transistor. Such transistor can be incorporated into, for example, complementary metal-oxide semiconductor (CMOS) circuitry.

The functions of transistors 33 and 53 are different, and accordingly problems associated with gates 18 and 20 can be somewhat different. For instance, a problem associated with transistor gates in a memory array (such as, for example, a dynamic random access memory (DRAM) array) is leakage current between source and drain regions, and a problem associated with peripheral transistor gates is the speed of a change from an off-current to an on-current. The above-mentioned problems can be differently affected by a thickness of a gate dielectric material. Accordingly, there has been an effort to vary the thickness of dielectric material 40 of the peripheral transistor 53 relative to the thickness of dielectric material 22 of memory array transistor 33. Ideally, dielectric material 22 would be as thin possible, and dielectric material 40 would be somewhat thicker. Presently, dielectric materials can be formed to thicknesses of as little as about 50 Angstroms, but it has proved difficult to reliably form the materials thinner than 50 Angstroms. Such difficulty results from the inherent size and spacing of atoms. For instance, a silicon structure will typically have about a 5.3 Angstrom separation between atoms. Accordingly, a gate dielectric comprising silicon and which is 50 Angstroms thick will have a maximum of 10 monolayers of silicon atoms. Thus, even small inhomogeneities within or between the monolayers can significantly impact the uniformity of a material comprising the layers, and accordingly destroy device operation of transistor gate devices formed utilizing such material.

It would be desirable to develop alternative methods and structures for controlling physical and electrical properties of transistor gates.

SUMMARY OF THE INVENTION

In one aspect, the invention encompasses integrated circuitry. Such circuitry includes a semiconductive material substrate and a first field effect transistor supported by the substrate. The first field effect transistor comprises a first transistor gate assembly which includes a first layer of conductively doped semiconductive material and only one layer of conductive nitride. The integrated circuitry further comprises a second field effect transistor supported by the substrate. The second field effect transistor comprises a second transistor gate assembly which includes a second layer of conductively doped semiconductor material and at least two layers of conductive nitride.

In another aspect, the invention encompasses a field effect transistor assembly. Such assembly includes a substrate and source/drain regions supported by the substrate. A channel region is defined between the source/drain regions, and the transistor assembly includes an insulative material along the channel region. The transistor assembly further includes a gate stack proximate the channel region. The gate stack includes a first conductive nitride layer separated from the channel region by the insulative material. The stack further includes a conductively doped semiconductive material proximate the first conductive nitride layer, and a second conductive nitride layer separated from the first conductive nitride layer by the conductively doped semiconductive material.

In yet other aspects, the invention encompasses methods of forming field effect transistors, and methods of forming integrated circuitry.

BRIEF DESCRIPTION OF THE DRAWINGS

Preferred embodiments of the invention are described below with reference to the following accompanying drawings.

FIG. 1 is a diagrammatic, schematic, cross-sectional view of a prior art semiconductor wafer fragment.

FIG. 2 is a diagrammatic, schematic, cross-sectional view of a semiconductor wafer fragment encompassed by the present invention.

FIG. 3 is a diagrammatic, cross-sectional, schematic, fragmentary view of a semiconductor wafer fragment at an initial step in a processing sequence utilized to form the construction of FIG. 2.

FIG. 4 is a view of the FIG. 3 wafer fragment shown at a step subsequent to that of FIG. 3.

FIG. 5 is a view of the FIG. 3 wafer fragment shown at a step subsequent to that of FIG. 4.

FIG. 6 is a view of the FIG. 3 wafer fragment shown at a step subsequent to that of FIG. 5.

FIG. 7 is a view of the FIG. 3 wafer fragment shown at a step subsequent to that of FIG. 6.

FIG. 8 is a diagrammatic, fragmentary, schematic, cross-sectional view of a semiconductor wafer fragment processed according to a second embodiment method of forming the construction of FIG. 2, and shown at an initial processing step.

FIG. 9 is a view of the FIG. 8 wafer fragment shown at a step subsequent to that of FIG. 8.

FIG. 10 is a diagrammatic, fragmentary, cross-sectional view of a semiconductor wafer fragment shown at an initial step of a processing sequence of the present invention for forming a field effect transistor.

FIG. 11 is a view of the FIG. 10 wafer fragment shown at a processing step subsequent to that of FIG. 10.

FIG. 12 is a view of the FIG. 10 wafer fragment shown at a processing step subsequent to that of FIG. 11.

FIG. 13 is a diagrammatic, fragmentary, cross-sectional view of a semiconductor wafer fragment shown at an initial step of a second embodiment processing sequence of the present invention for forming a field effect transistor.

FIG. 14 is a view of the FIG. 13 wafer fragment shown at a processing step subsequent to that of FIG. 13.

FIG. 15 is a view of the FIG. 13 wafer fragment shown at a processing step subsequent to that of FIG. 14.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

This disclosure of the invention is submitted in furtherance of the constitutional purposes of the U.S. Patent Laws “to promote the progress of science and useful arts” (Article 1, Section 8).

FIG. 2 shows a semiconductor wafer fragment 10 a comprising transistor structures encompassed by the present invention. In referring to FIG. 2, some structures will be labeled with similar numbering as was utilized above in describing the prior art, with the suffix “a” utilized to indicate structures shown in FIG. 2.

Wafer fragment 10 a comprises a memory array region 12 a, and a region 14 a peripheral to the memory array region. Wafer fragment 10 a includes a substrate 16 a which can comprise, for example, monocrystalline silicon. A first field effect transistor assembly 100 is formed within peripheral region 14 a and supported by substrate 16 a, and a second field effect transistor assembly 102 is formed with memory array region 12 a and supported by substrate 16 a. First field effect transistor assembly 100 comprises first source/drain regions 104, and second transistor assembly 102 comprises second source/drain regions 106. A first channel region 107 is defined to extend between first source/drain regions 104, and a second channel region 109 is defined to extend between second source/drain regions 106. Source/drain regions 104 can comprise materials similar to those described above regarding source/drain regions 50 of FIG. 1, and source/drain regions 106 can comprise materials similar to those discussed above regarding source/drain regions 32 of FIG. 1.

First field effect transistor assembly 100 comprises a first transistor gate assembly 110 formed along first channel region 107, and comprises spacers 122 formed adjacent the gate assembly 110. Spacers 122 can comprise, for example, insulative materials such as silicon dioxide or silicon nitride.

Gate assembly 110 includes a stack comprising a first insulative material 112, a first conductively doped semiconductive material 114, and a first conductive nitride material 116. In the shown embodiment, a lowestmost portion of the stack consists of materials 112, 114 and 116.

Insulative material 112 can comprise, for example, silicon dioxide, silicon nitride, SiN_(x)O_(y), or tantalum pentoxide. Material 112 can define a layer having a thickness of from about 15 Å to about 75 Å. Material 112 can, for example, define a layer comprising a construction identical to that of the prior art gate dielectric 40 described above with reference to FIG. 1.

Conductively doped semiconductive material 114 can comprise, for example, conductively doped polysilicon. Such polysilicon is preferably doped to a concentration of at least 10¹⁹ atoms/cm³ with either n-type or p-type conductivity enhancing dopant. It is noted that an effective dopant concentration range (i.e., a dopant concentration range which renders the polysilicon conductive) within polysilicon material 114 can be increased relative to the effective dopant range of prior transistor structures due to a diminished depletion effect resulting from incorporation of conductive nitride material 116. Specifically, an effective dopant concentration range of a prior conductively doped polysilicon material in a transistor gate (such as material 42 of FIG. 1) is typically from 10²⁰ atoms/cm³ to about 10²¹ atoms/cm³, whereas an effective dopant concentration of doped polysilicon material 114 can be from 10¹⁹ atoms/cm³ to about 10²¹ atoms/cm³. The layer defined by material 114 is preferably from about 100 Å thick to about 800 Å thick, and can be, for example, about 500 Å thick.

Conductive nitride material 116 can comprise, for example, a metal nitride (such as, for example, titanium nitride), and preferably defines a layer that is from about 25 Å thick to about 100 Å thick. Such layer can be, for example, about 40 Å thick, and can be formed by, for example, chemical vapor deposition, plasma enhanced chemical vapor deposition, or sputter deposition.

Materials 112, 114 and 116 are stacked from channel region 107 in the order of material 112 first, material 114 second, and material 116 third. Accordingly, conductively doped semiconductive material 114 is separated from substrate 16 a by insulative material 112, and conductive nitride material 116 is separated from insulative material 112 by conductively doped semiconductive material 114.

In addition to the materials described above, gate assembly 110 comprises a metal-containing material 118, and an insulative cap 120. Metal-containing material 118 can comprise, for example, tungsten, and can, for example, have a thickness of from about 350 Å to about 600 Å. Further, metal-containing material 118 can consist essentially of an elemental form of a metal, such as, for example, elemental tungsten.

Insulative cap 120 can comprise, for example, silicon nitride or silicon dioxide, and can, for example, define a layer having a thickness of from about 350 Å to about 600 Å. Also, insulative cap 120 can comprise a stack of insulative materials, such as, for example, a stack comprising DARC and nitride.

Second field effect transistor assembly 102 comprises a second transistor gate assembly 128 formed along second channel region 109, and comprises spacers 142 formed adjacent the gate assembly 128. Spacers 142 can comprise, for example, insulative materials such as silicon dioxide or silicon nitride.

Gate assembly 128 comprises a second insulative material 130, a second conductive nitride material 132, a second conductively doped semiconductive material 134, a third conductive nitride material 136, a second metal-containing material 138, and a second insulative cap 140. In the shown embodiment, conductively doped semiconductive material 134 is between and against layers defined by conductive nitride materials 132 and 136.

Second insulative material 130 can comprise an identical composition as first insulative material 112. Conductive nitride materials 132 and 136 can comprise constructions identical to that described above for material 116, and accordingly can comprise titanium nitride and thicknesses of from about 25 Å to about 100 Å. Semiconductive material 134 can comprise a construction identical to that described above for material 114, and accordingly can comprise conductively doped polysilicon. Metal-containing material 138 and insulative cap 140 can comprise identical structures as described above regarding metal-containing material 118 and insulative cap 120. Accordingly, material 138 can comprise, for example tungsten, and insulative cap 140 can comprise, for example, silicon dioxide, silicon nitride, or a stack of insulative materials.

Transistor assembly 100 is preferably constructed to enable a fast transition from an off-state to an on-state, and vice versa, while transistor assembly 102 is preferably configured to reduce leakage between the source and drain regions 106.

A difference between gate assembly 110 of device 100 and gate assembly 128 of device 102 is that assembly 110 comprises only one layer of conductive nitride, whereas assembly 102 comprises more than one layer of conductive nitride. Another difference between assembly 110 and assembly 102 is that the conductively doped semiconductive material 114 of assembly 110 is not between any layers of conductive nitride, whereas the conductively doped semiconductive material 134 of assembly 128 is between a pair of conductive nitride layers.

It is noted that assembly 128 can comprise more than the two shown nitride layers defined by materials 132 and 136, and that such layers can themselves comprise stacks of two or more conductive nitride materials. In other words, materials 132 and 136 can comprise either relatively homogeneous compositions throughout the layers defined by materials 132 and 136, or can comprise heterogenous compositions. For instance, one or both of materials 132 and 136 can comprise differing compositions of metal and nitrogen throughout its thickness so that layers defined by one or both of materials 132 and 136 can alternatively be considered as comprising a plurality of different conductive nitride layers. Materials 132 and 136 are to be understood to comprise conductive nitride, unless it is specifically stated that such materials consist essentially of conductive nitride.

It is also noted that assembly 110 can comprise more than the single shown layer defined by conductive nitride material 116. Similarly to the above-discussed materials 132 and 136, material 116 can comprise either a relatively homogeneous composition throughout the layer defined by material 116, or can comprise a heterogenous composition. For instance, material 116 can comprise differing compositions of metal and nitrogen throughout its thickness so that a layer defined by material 116 can alternatively be considered as comprising a plurality of different conductive nitride layers. Material 116 is to be understood to comprise conductive nitride, unless it is specifically stated that such material consists essentially of conductive nitride.

A first embodiment method of forming the structure of FIG. 2 is described with reference to FIGS. 3-7. In referring to FIGS. 3-7, similar numbering will be utilized as was used above in describing FIG. 2.

Referring to FIG. 3, semiconductive wafer fragment 10 a is shown at an initial step of the processing sequence. Fragment 10 a comprises substrate 16 a, and insulative materials 112 and 130 formed thereover. Preferably, insulative materials 112 and 130 are portions of a continuous insulative structure formed over substrate 16 a, and accordingly have the same chemical composition as one another. Insulative materials 112 and 130 can comprise, for example, silicon dioxide, and can be formed by either growing a layer of silicon dioxide over a silicon substrate 16 a, or by chemical vapor deposition. Alternatively, and by way of example only, materials 112 and 130 can comprise tantalum pentoxide, and can be formed by chemical vapor deposition over substrate 16 a.

Conductively doped semiconductive material 114 is shown selectively formed over peripheral region 14 a, and not over memory array region 12 a. Such can be accomplished by, for example, chemical vapor deposition and doping of polysilicon, and subsequent photolithographic processing to pattern the conductively doped polysilicon to remain only over region 14 a.

Referring to FIG. 4, layers comprising conductive nitride material 116 and 132 are formed over regions 14 a and 12 a, respectively. Preferably, such layers comprise a common conductive nitride material, such as, for example, titanium nitride, and are formed together, such as in a common chemical vapor deposition process.

Referring to FIG. 5, conductively doped semiconductor material 134 and a layer of second conductive nitride material 136 are formed over memory array region 12 a. Material 134 can be formed by, for example, chemical vapor deposition of polysilicon and subsequent doping of the polysilicon. Conductive nitride material 136 can be formed by, for example, chemical vapor deposition of titanium nitride. Layers defined by materials 134 and 136 can be patterned to be only over region 12 a, and not over region 14 a, by, for example, photolithographic processing. In alternative embodiments of the invention (not shown), materials 134 and 136 could be left over region 14 a as well as over region 12 a during subsequent processing.

Referring to FIG. 6, metal layers 118 and 138 are formed over regions 14 a and 12 a, respectively, and insulative cap layers 120 and 140 are formed over metal layers 118 and 138, respectively. Metal layers 118 and 138 can comprise a common material, and can be formed in a common processing step. For instance, metal layers 118 and 138 can comprise tungsten, and can be formed in a common sputtering process. Insulative cap layers 120 and 140 can comprise common constructions and can be formed by common processing. In the shown embodiment, insulative cap layers 120 and 140 comprise stacks of a DARC material 160, a silicon nitride material 162, and another DARC material 164.

Materials 112, 114, 116, 118 and 120 form a first stack 170, while materials 130, 132, 134, 136, 138 and 140 form a second stack 172. A masking material 180 is formed over stacks 170 and 172, and patterned into blocks. Material 180 can comprise, for example, photoresist, and can be patterned utilizing photolithographic processing.

Referring to FIG. 7, a pattern is transferred from masking material 180 to underlying stacks 170 and 172. Such transfer can be accomplished by, for example, etching of the material of stacks 170 and 172. The etching converts stacks 170 and 172 into patterns corresponding to gate stacks 110 and 128, respectively. Stacks 110 and 128 can be incorporated into the structures of FIG. 2 by formation of spacers and source/drain regions proximate the stacks.

Another method of forming the structures of FIG. 2 is described with reference to FIGS. 8 and 9. In referring to FIGS. 8 and 9, identical numbering will be used as was utilized above in describing the embodiment of FIGS. 3-7.

Referring to FIG. 8, insulative materials 112 and 130 are formed over substrate 16 a in regions 14 a and 12 a, and titanium nitride material 132 is formed over insulative material 130. If material 112 comprises silicon dioxide, any titanium nitride formed over material 112 can be removed with an etch selective for titanium nitride relative to silicon dioxide.

Referring to FIG. 9, materials 114, 116, 118 and 120 are formed over substrate 16 a in peripheral region 14 a, and materials 134, 136, 138 and 140 are formed over substrate 16 a in region 12 a. Preferably, materials 114 and 134 are the same composition and are formed in a common processing step. Such processing step can comprise, for example, chemical vapor deposition of polysilicon and doping of such polysilicon with a conductivity-enhancing dopant. Also preferably, materials 116 and 136 are the same composition and are formed in a common processing step. Such common processing step can comprise, for example, chemical vapor deposition of titanium nitride, plasma enhanced chemical vapor deposition of titanium nitride, or sputter deposition of titanium nitride. Further, materials 118 and 138 preferably are the same composition and are formed in a common processing step. Such common processing step can comprise, for example, sputter deposition of tungsten. Finally, materials 120 and 140 are preferably the same composition and are formed in common processing steps, such as the steps described above with reference to FIG. 6.

Materials 112, 114, 116, 118 and 120 form a first stack 170, while materials 130, 132, 134, 136, 138 and 140 form a second stack 172. A patterned masking material 180 is formed over stacks 170 and 172, and can be utilized to transfer a pattern to stacks 170 and 172 in processing of the type described above with reference to FIG. 7. Such processing will form gate stacks, and such gate stacks can be incorporated into transistor assemblies of the type described with reference to FIG. 2.

The transistor device 102 described above with reference to FIG. 2 is an exemplary transistor device of the present invention. Another exemplary transistor device is described with reference to FIGS. 10-12. In referring to FIGS. 10-12, similar numbering to that utilized above in FIG. 2 will be used, with the suffix “b” utilized to indicate structures referred to in FIGS. 10-12.

Referring to FIG. 10, a semiconductive wafer fragment 10 b is illustrated at an initial step in formation of a transistor device. Wafer fragment 10 b comprises a substrate 16 b having an insulative material 130 b formed thereover. A gate stack 128 b is formed over insulative material 130 b. Gate stack 128 b comprises a first conductive nitride material 132 b, a conductively doped semiconductive material 134 b, a second conductive nitride material 136 b, and a metal-containing material 138 b. Stack 128 b further comprises an insulative cap 140 b formed over metal-containing material 138 b. Materials 130 b, 132 b, 134 b, 136 b, 138 b and 140 b can be identical to the materials 130, 132, 134, 136, 138 and 140, respectively, of FIG. 2.

Referring to FIG. 11, stack 128 b is exposed to etching conditions which selectively etch the layers defined by conductive nitride materials 132 b and 136 b relative to the layer defined by semiconductive material 134 b and the layer defined by metal 138 b. In a particular embodiment, materials 132 b and 136 b comprise titanium nitride, material 134 b comprises conductively doped polysilicon, and material 138 b comprises tungsten. In such embodiment, the selective etching of FIG. 11 can comprise, for example, exposing stack 128 b to hydrofluoric acid. It is noted that the hydrofluoric acid can etch insulative material 130 b in embodiments in which material 130 b comprises silicon dioxide.

After the exposure to hydrofluoric acid, the layer defined by semiconductive material 134 b comprises a first lateral width “x”, and the layers defined by conductive nitride materials 132 b and 136 b comprise lateral widths “y” and “z”, respectively. The lateral widths “y” and “z” are less than lateral width “x”, and are approximately equal to one another. By “approximately equal”, it is meant that the layers defined by materials 132 b and 136 b started as having the same lateral widths (due to their incorporation into the same gate stack), and were exposed to common etching conditions. Accordingly, such layers have lateral widths which are equal to each other to the extent achievable by exposing the layers to equivalent etching conditions.

The layer defined by material 132 b has edges 133 b, and the layer defined by material 136 b has edges 137 b. Further, the layer defined by material 134 b has edges 135 b. After the etching of materials 132 b and 136 b, edges 133 b and 137 b are inset relative to edges 135 b of semiconductive material 134 b.

Referring to FIG. 12, insulative sidewall spacers 142 b are formed along sidewalls of gate stack 128 b. Spacers 142 b comprise an insulative material which extends from inset edges 133 b and 137 b to at least the edges 135 b of material 134 b. The insulative material of spacers 142 b can comprise, for example, silicon nitride or silicon dioxide.

After formation of spacers 142 b, a conductivity enhancing dopant can be implanted into substrate 16 b proximate gate stack 128 b to form source/drain regions 106 b.

The construction of FIG. 12 effectively has an undercut etch of titanium nitride material 132 b relative to semiconductive material 134 b. Such undercut etch enables a thicker dielectric to be provided at the edge of the gate (i.e., underneath a portion of semiconductive material 134 b that overhangs beyond edge 133 b of nitride layer 132 b). The thicker dielectric at the edge of the gate can reduce gate-induced drain leakage (GIDL) and hot carrier effects of a transistor device. Thus, the thicker dielectric can make a transistor device less leaky and more reliable.

Yet another exemplary transistor device is described with reference to FIGS. 13-15. In referring to FIGS. 13-15, similar numbering to that utilized above in FIGS. 10-12 will be used, with the suffix “c” utilized to indicate structures referred to in FIGS. 13-15.

Referring to FIG. 13, a semiconductive wafer fragment 10 c is illustrated at an initial step in formation of a transistor device. Wafer fragment 10 c comprises a substrate 16 c having an insulative material 130 c formed thereover. A gate stack 128 c is formed over insulative material 130 c. Gate stack 128 c comprises a first conductive nitride material 132 c, a conductively doped semiconductive material 134 c, a second conductive nitride material 136 c, and a metal-containing material 138 c. Stack 128 c further comprises an insulative cap 140 c formed over metal-containing material 138 c. Materials 130 c, 132 c, 134 c, 136 c, 138 c and 140 c can be identical to the materials 130, 132, 134, 136, 138 and 140, respectively, of FIG. 2.

Referring to FIG. 14, stack 128 c is exposed to conditions which selectively form extensions 160 over the edges of the material of layer 134 c. In a particular embodiment, materials 132 c and 136 c comprise titanium nitride, material 134 c comprises conductively doped polysilicon, and material 138 c comprises tungsten. In such embodiment, the selective formation of extensions 160 can comprise utilization of conditions which oxidize polysilicon faster than titanium nitride and tungsten to accordingly grow silicon dioxide over the exposed edges of the polysilicon.

After the formation of extensions 160, the layer defined by material 132 c has edges 133 c, the layer defined by material 136 c has edges 137 c, and a layer defined by material 134 c and extensions 160 has edges 135 c. Edges 133 c and 137 c are inset relative to edges 135 c of semiconductive material 134 c. Accordingly, the layer defined by semiconductive material 134 c and extensions 160 comprises a first lateral width which is greater than the lateral widths of layers 132 c and 136 c.

Referring to FIG. 15, insulative sidewall spacers 142 c are formed along sidewalls of gate stack 128 c. Spacers 142 c comprise an insulative material which extends from inset edges 133 c and 137 c to at least the edges 135 c. The insulative material of spacers 142 c can comprise, for example, silicon nitride or silicon dioxide.

After formation of spacers 142 c, a conductivity enhancing dopant can be implanted into substrate 16 c proximate gate stack 128 c to form source/drain regions 106 c.

The transistor device structures described above with reference to FIGS. 2, 12 and 15 incorporate titanium-nitride-containing layers into gate stacks to enable, among other things, low threshold voltage control of transistor devices formed from the gate stacks. Such can enable advantages to be realized with the gate stacks that were previously sought through reduction, or other adjustment, of gate dielectric material thickness.

In compliance with the statute, the invention has been described in language more or less specific as to structural and methodical features. It is to be understood, however, that the invention is not limited to the specific features shown and described, since the means herein disclosed comprise preferred forms of putting the invention into effect. The invention is, therefore, claimed in any of its forms or modifications within the proper scope of the appended claims appropriately interpreted in accordance with the doctrine of equivalents. 

What is claimed is:
 1. A method of forming a field effect transistor, comprising: providing a semiconductive material substrate; forming a layer of first insulative material proximate the substrate; forming a first conductive nitride layer, the first conductive nitride layer being spaced from the substrate by the first insulative material; forming a conductively doped semiconductive material layer, the conductively doped semiconductive material being spaced from the insulative material by the first conductive nitride layer; and forming a second conductive nitride layer, the second conductive nitride layer being spaced from the first conductive nitride layer by the conductively doped semiconductive material layer.
 2. The method of claim 1 wherein the conductive nitride layers comprise titanium nitride.
 3. The method of claim 1 wherein the conductively doped semiconductive material comprises conductively doped polysilicon.
 4. The method of claim 1 wherein the first insulative material comprises one or both of silicon dioxide and tantalum pentoxide.
 5. The method of claim 1 further comprising etching the conductive nitride layers with an etch selective for the conductive nitride relative to the conductively doped semiconductive material, the etching insetting edges of the conductive nitride layers relative to edges of the conductively doped semiconductive material.
 6. The method of claim 5 wherein the conductively doped semiconductive material comprises conductively doped polysilicon and wherein the conductive nitride layers comprise titanium nitride, the etching comprising exposing the titanium nitride to hydrofluoric acid.
 7. The method of claim 5 further comprising forming a second insulative material proximate the inset edges of the conductive nitride layers, the second insulative material extending from the inset edges to at least the edges of the conductively doped semiconductive material.
 8. The method of claim 1 further comprising forming extensions over edges of the conductively doped semiconductive material; after the extensions are formed, the edges of the conductive nitride layers being inset relative to edges of a layer comprising the extensions and the conductively doped semiconductive material.
 9. The method of claim 8 wherein the conductively doped semiconductive material comprises conductively doped polysilicon and wherein the conductive nitride layers comprise titanium nitride, the forming extensions comprising oxidizing the conductively doped polysilicon.
 10. A method of forming integrated circuitry, comprising: providing a semiconductive material substrate; forming a first field effect transistor proximate the substrate, the forming the first field effect transistor comprising: forming a first insulative material over the substrate; forming a first conductively doped semiconductive material over the first insulative material; forming a first conductive nitride material over the first conductively doped semiconductive material; patterning the first conductively doped semiconductive material and first conductive nitride material as a first gate stack; and forming first source/drain regions proximate the first gate stack; forming a second field effect transistor proximate the substrate, the forming the second field effect transistor comprising: forming a second insulative material proximate the substrate; forming a second conductive nitride material over the second insulative material; forming a second conductively doped semiconductive material over the second conductive nitride layer; forming a third conductive nitride material over the second conductively doped semiconductive material; patterning the second conductively doped semiconductive material, second conductive nitride material, and third conductive nitride material as a second gate stack; and forming second source/drain regions proximate the second gate stack.
 11. The method of claim 10 wherein the first, second and third conductive nitride materials comprise titanium nitride.
 12. The method of claim 10 wherein: the first and second insulative material are formed in a common step and comprise silicon dioxide; and the first and second conductively doped semiconductive materials are formed in a common step and comprising conductively doped polysilicon.
 13. The method of claim 12 wherein the first and third conductive nitride materials are formed in a common step.
 14. The method of claim 12 wherein the first and third conductive nitride materials are formed in a common step and comprise titanium nitride.
 15. The method of claim 10 wherein the second and third conductive nitride materials define a pair of spaced conductive nitride layers, the method further comprising, after forming the second and third conductive nitride materials, etching the second and third conductive nitride materials with an etch selective for the second and third conductive nitride materials relative to the second conductively doped semiconductive material, the etching insetting edges of the spaced conductive nitride layers relative to edges of the conductively doped semiconductive material.
 16. The method of claim 15 wherein the second conductively doped semiconductive material comprises conductively doped polysilicon and wherein the pair of conductive nitride layers comprise titanium nitride, the etching comprising exposing the titanium nitride to hydrofluoric acid. 